Description In the absence of magnesium oxide and a promoter under the conditions of NA-22, EVA foam manufacturer agent 64 to 15 parts, the amount of time in order that TAC and DCP speed and EVA foam manufacturer to achieve the best balance of curing rate. Thus also proved less sulfur and sulfur are making the appearance of anomalies over this table 4EVA foam manufacturer and agent 64 is 9 when the results were consistent.

2.6 EVA foam manufacturer agent of

In the basic formulation study EVA foam manufacturer agent 64 on the experimental results of different amounts, see Table 6. From Table 6, EVA foam manufacturer to increase the amount of agent 64, EL increases proportional two persons, with the same mechanism of EVA foam manufacturer. To 16 copies, because of gas evolution is too large, the expansion of the specimen mold, that is not a piece burst. Description In this formula system, EVA foam manufacturer limits the amount of agent 64 to 16 copies.

3 Conclusions

EVA FOAM MANUFACTURER / CPE for the vulcanization system expansion EVA foam manufacturer may be combined in any proportion; with EVA FOAM MANUFACTURER / CPE = 60/40 when, EVA foam manufacturer best. Using EVA FOAM MANUFACTURER / CPE = 40/60, an amount of 180 parts of filler, the mill operation process best.

Vulcanization system, an amount of 11 parts of magnesium oxide or not when the optimum appearance. NA-22 without accelerator and magnesium oxide can also be cured, but: ① DCP dosage range is narrow, adding accelerator NA-22 to 1 parts, and vice versa. ② TAC dosage of 1.5 parts, DCP amount of 2.5 to 2.75 parts, EVA foam manufacturer agent 64 when the amount of 15 parts, EVA foam manufacturer to achieve the best speed and the cure rate.